Influence of denture brushing on the surface properties and color stability of CAD-CAM, thermoformed, and conventionally fabricated denture base resins

Purpose: To assess the influence of denture brushing on the surface roughness, hardness, and color stability of conventional, thermoformed, and CAD-CAM denture base materials. Materials and Methods: Seven different denture base materials were included in this study; conventional heat-polymerized acrylic resin (PMMA) served as control, polyamide, acetal, two categories of milled acrylic discs (AvaDent and IvoCad), and two categories of 3D-printed resins (NextDent and FormLabs). The specimens were constructed according to manufacturers’ instructions and then subjected to simulated brushing (20,000 cycles). According to the brushing method, the specimens were split into three groups, no brushing, brushing with water, and brushing with toothpaste. Surface roughness, hardness, and color change were evaluated before and after brushing. Collected data were analyzed using ANOVA, and post-hoc Tukey's tests (α = 0.05). Results: A significant difference was noted between the surface roughness of the tested materials before and after denture brushing (p < 0.05), and milled resin showed the least Ra values. Denture brushing with water significantly increased the Ra of PMMA (p = 0.004) and IvoCad (p = 0.032), while brushing using toothpaste did not show a significant increase. The brushing protocols did not alter the hardness of tested materials except that of PMMA (p = 0.001). The color stability of the tested materials showed comparable results with both brushing protocols. Conclusion: The tested properties showed variations between the types of denture base resins. Hardness and color stability of CAD-CAM and thermoformed denture base resins were not altered by denture brushing and showed comparable results with both brushing methods. Surface roughness was the only property that showed alteration after denture brushing.